Thin laminated glass for windscreen

ABSTRACT

A laminated glazing includes at least one outer glass sheet, an inner glass sheet and a polymeric insert located between the two glass sheets, in which the inner sheet has a thickness of not more than 1.5 mm, the outer glass sheet is a glass sheet of different chemical composition from that of the inner sheet, the difference between the temperatures Tp1 and Tp2 being less than 80° C., the temperature Tp1 being defined as the mean between the upper annealing temperature and the softening point of the outer glass sheet and the temperature Tp2 being defined as the mean between the upper annealing temperature and the softening point of the inner glass sheet.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is the U.S. National Stage of PCT/FR2014/052685, filedOct. 22, 2014, which in turn claims priority to French Application No.1360326, filed Oct. 23, 2013. The contents of all of these applicationsare incorporated herein by reference in their entirety.

The present invention relates to laminated glazing consisting of atleast two thin sheets of glass. The invention relates more particularlyto a laminated glazing for use in the motor vehicle sector, especiallyas a windshield.

Laminated glazings are commonly used in the motor vehicle, aeronauticalor building sector, since they have the advantage of being “safety”glazings. They consist of at least two sheets of glass linked togetherby an insert layer made of plastic, generally of polyvinyl butyral(PVB). Conventionally, the glazings used for windshields areasymmetrical and consist of two sheets of silicon-sodium-calcium glass,of different thicknesses, the outer sheet generally being thicker thanthe inner sheet. To improve the mechanical strength of this type ofglazing, it is known practice to reinforce the constituent glass sheetsby tempering them and thus creating a surface zone in compression and acentral zone in tension. U.S. Pat. No. 3,558,415 describes a bentlaminated glazing in which the outer and inner glass sheets have beenchemically tempered so as to have a surface zone in compression. PatentGB 1 339 980 describes a windshield glazing in which only the outerglass sheet is chemically tempered.

A problem regularly encountered in the motor vehicle sector relates tothe weight of the glazings. The windshields currently manufacturedtypically have an outer sheet with a thickness of between 2.1 and 2.6 mmand an inner sheet with a thickness of between 1.6 and 2.1 mm. It iscurrently sought to reduce the weight of glazings without, however,compromising the mechanical strength properties. Patent applications WO2012/051 038 and WO 2012/177 426 describe laminated glasses in which theglass sheets have a thickness of less than 2 mm and at least one of theglass sheets is chemically tempered. The reduction in thickness of theconstituent glass sheets of a windshield allows its weight to be reducedbut may give rise to mechanical problems, especially an increase in itsfragility when it is exposed to projections of gravel. The solutionproposed by the documents cited above for improving the mechanicalstrength consists in chemically tempering the outer glass sheet. Theprocess of chemical tempering, or ionic exchange, consists of thesurface replacement of an ion of the glass sheet (generally an ion of analkali metal such as sodium) with an ion of larger ionic radius(generally an ion of another alkali metal such as potassium) and increating residual compression stresses at the surface of the sheet, downto a certain depth. This is a relatively expensive and long process andis consequently poorly compatible with a continuous industrial process.

A step of bending glass sheets is essential for the desiredapplications. Bending makes it possible to give the glass sheets acurvature and thus to facilitate the assembling of the various sheetsconstituting the laminated glazing. Many bending processes may be used.Mention will be made, for example, of bending by gravity, bending bypassing between conveying rollers, bending by pressing against a solidform, performed either using a frame or by suction. The simultaneousbending of glass sheets on a framework by gravity and/or partially bypressing (as described in patent applications EP 0 448 447, WO 2004/087590, WO 02/064 519 or WO 2006/072 721) are techniques used forsimultaneously bending the two glass sheets intended to form a bentlaminated glazing such as a haulage vehicle windshield. The two glasssheets laid one on the other are supported along their marginalextremities substantially horizontally by a frame having the desiredprofile, i.e. the profile corresponding to the final profile of the twobent glass sheets. Thus supported, the two glass sheets pass through abending oven, generally an oven having different temperature zones. Whenthe two glass sheets are of different chemical composition, theirbehavior during this bending step may be different, and the risk ofappearance of defects or of residual stresses is consequently increased.One solution proposed when the physicochemical properties and thethicknesses of the glass sheets are different is described in patentapplication GB 2 078 169 and consists in reversing the order of theglass sheets during the bending process relative to the order that thesesame sheets have during the assembly phase.

It would be useful, for the sake of the optical quality of the products,the cost, the weight and simplification of the technology, to haveavailable a thin laminated glass whose mechanical strength is compatiblewith the desired applications, and which consists of glass sheets thatcan be simultaneously bent, without the need to modify the order of theglass sheets between the bending step and the assembly step.Simultaneous bending and direct assembly, without reversal of thesheets, is all the more interesting since the constituent sheets of theglazing are of low thickness.

The present invention falls within this context, the subject of which isa laminated glazing which comprises at least one outer glass sheet, aninner glass sheet and a polymeric insert located between the two glasssheets, in which the inner sheet has a thickness of not more than 1.5 mmand the outer glass sheet is a glass sheet of different chemicalcomposition from that of the inner sheet,

the difference ΔTp between the temperatures Tp1 and Tp2 being less than80° C., preferably less than 70° C. and even more preferentially lessthan 60° C.;

the temperature Tp1 being defined as the average between the upperannealing temperature and the softening point of the outer glass sheetand the temperature Tp2 being defined as the average between the upperannealing temperature and the softening point of the inner glass sheet,the general formula defining the temperature Tp beingTp=(T _(softening) +T _(annealing))/2

the upper annealing temperature corresponding to the temperature atwhich the viscosity of the glass is 10¹³ poises and the softening pointcorresponding to the temperature at which the viscosity of the glass is10^(7.6) poises.

The temperature Tp1 which corresponds to the average of the temperaturesdefined above for the outer sheet is, according to the invention, higherthan the temperature Tp2, corresponding to the average of thetemperatures defined above for the inner sheet.

The temperature Tp1 is higher than the temperature Tp2, and as such thedifference ΔTp between the temperatures Tp1 and Tp2 is positive.

The difference ΔTp is thus between 0 and 80° C.

In the present invention, the term “outer” is used for everythingrelating to the exterior of the device receiving the glazing. The outerglass sheet is consequently that which is positioned facing the exteriorof the cockpit. Conversely, the term “inner” is used for that relatingto the interior of the device receiving the glazing. An inner sheet of alaminated glazing corresponds to the sheet that is placed facing theinterior of the cockpit.

The inventors have demonstrated that it is possible to produce alaminated glazing with a total thickness of less than 4.5 mm, or even 4mm, with two glass sheets of different chemical composition and whichcan be bent simultaneously, and then assembled directly, withoutreversal of the order of the glass sheets. Thus, the product is obtainedwithout the need to bend each of the two sheets separately, despitetheir different chemical composition. It conserves satisfactorymechanical strength for use as a motor vehicle windshield. An importantconsequence for the final product is especially its lightened weight,leading to lightening of the weight of the vehicle and reducedconsumption. An asymmetric assembly, in thickness and in chemicalcomposition, combining an outer glass sheet and a very thin inner glasssheet, advantageously makes it possible to obtain strong, lightenedwindshields.

Each glass sheet, depending on its composition, is characterized by itsupper annealing temperature (or simply “annealing temperature”) and itssoftening point (also known as the “Littleton temperature”).

The annealing temperature corresponds to the temperature for which theviscosity of the glass is high enough for disappearance of the stressesto be able to take place entirely within a given time (stress relaxationtime of about 15 minutes). It is occasionally referred to as the “stressrelaxation temperature”. This temperature corresponds to the moment atwhich the viscosity of the liquid η is 10¹³ poises. Measurements of thistemperature are conventionally performed according to standard NFB30-105.

The softening point is defined as being the temperature at which a glassyarn with a diameter of about 0.7 mm and a length of 23.5 cm lengthensby 1 mm/minute under its own weight (standard ISO 7884-6). Thecorresponding viscosity is 10^(7.6) poises.

The temperature Tp is defined in the following manner:Tp=(T _(softening) +T _(annealing))/2

Each glass sheet is characterized, as a function of its composition, bya temperature Tp. The laminated glazing according to the presentinvention must be composed of two glass sheets whose temperatures Tp areas close as possible, to satisfy the desired requirement forsimultaneous bending. For applications in the motor vehicle sector andespecially as windshields, it is important to ensure that the processfor manufacturing the laminated glazing, especially the bending orforming steps, do not produce defects in the glazing.

The laminated glazing according to the present invention has theadvantage of being able to be bent without increasing the risk ofcreating residual stresses or optical defects. The two constituent glasssheets of the glazing have a different chemical composition but are suchthat it is possible to bend them together without complicating theprocess on account of the difference in chemical composition of the twoglass sheets, and especially without the need to reverse the order ofthe glass sheets between the bending step and the assembly step.

The outer glass sheet has a thickness of not more than 2.1 mm andpreferably not more than 1.6 mm. Thus, this relatively low thickness ofthe outer sheet also contributes toward lightening the weight of thelaminated glazing. The laminated glazing according to the presentinvention has good mechanical strength and good durability of theglazing after damage by projection of gravel. The risks of breakageduring the subsequent application of heat gradients on embrittledglazings, especially, for example, during the deicing of a windshield,are thus reduced.

The chemical composition of the outer sheet is different from that ofthe inner glass sheet. Advantageously, the laminated glass according tothe present invention has an outer glass sheet made of “special glass”whose composition is chosen from the compositions given below.

The glass compositions below mention only the essential constituents.They do not give the minor elements of the composition, for instance theconventionally used refining agents such as arsenic, antimony, tin andcerium oxides, metal halides or sulfides or coloring agents, especiallysuch as iron oxides, cobalt, chromium, copper, vanadium, nickel andselenium oxides, which are most often necessary for glass applicationsin motor vehicle glazing.

According to one embodiment, the outer glass sheet has a chemicalcomposition of borosilicate type. The outer glass sheet may be such thatits chemical composition comprises the following oxides in the weightcontent ranges defined below:

SiO₂ 75-85%, Al₂O₃  2-3%, B₂O₃ 10-15%, Na₂O + K₂O  3-7%.

According to another embodiment, the outer glass sheet may also be ofthe sodium aluminosilicate type and such that its chemical compositioncomprises the following oxides in the weight content ranges definedbelow:

SiO₂ 55-71%,  Al₂O₃ 2-15%, preferably 4-15% Na₂O 9-18% MgO 2-11% K₂O1-15% B₂O₃  0-5%, CaO  0-5% SnO₂  0-5%

This type of glass is described, for example, in patent EP-B-0 914 298.

The laminated glazing is preferably asymmetrical in thickness: thethickness of the outer glass sheet is greater than the thickness of theinner glass sheet.

According to one embodiment, the outer glass sheet is a non-reinforcedglass sheet.

For the purposes of the present invention, the term “non-reinforced”means that the sheet is neither chemically reinforced nor thermallyreinforced, before bending. As they are not chemically reinforced, thesheets normally do not contain an overconcentration of an oxide of analkali metal such as Na or K at the surface relative to the core.Nevertheless, certain stresses, advantageously in compression, mayappear in the glass and result from the assembly with the polymericinsert.

It is, however, possible, if the user so desires and if the glass sopermits, to chemically reinforce the glass sheets by tempering.

The inner sheet of the laminated glazing has a thickness of not morethan 1.5 mm. Preferentially, this sheet has a thickness of not more than1.1 mm, or even is less than 1 mm. Advantageously, the inner glass sheethas a thickness of less than or equal to 0.7 mm. The thickness of theglass sheet is at least 50 μm.

Preferably, the inner glass sheet has a chemical composition ofsilicon-sodium-calcium type.

Conventionally, the inner glass sheet is a glass ofsilicon-sodium-calcium composition such that it comprises the followingoxides in the weight ranges defined below:

SiO₂ 65-75%,  Na₂O 10-20%   CaO 5-15%,  Al₂O₃ 0-5%, K₂O 0-5%  MgO 0-5%.

For reasons of cost, it is effectively more advantageous to manufacturea laminated glazing with only one sheet of special glass.Advantageously, the coloring and/or functionality of the laminatedglazing are provided by means of the inner glass sheet. To do this, aninner glass sheet that has optical and/or energy functions may bechosen, for example by using a tinted inner glass sheet. According to apreferred embodiment, the laminated glazing according to the presentinvention comprises an inner sheet of silicon-sodium-calcium type(ordinary glass) and an outer sheet made of special glass, which is notof silicon-sodium-calcium type.

The polymeric insert may consist of one or more layers of thermoplastic.It may especially be made of polyurethane, polycarbonate, polyvinylbutyral (PVB), polymethyl methacrylate (PMMA), ethylene-vinyl acetate(EVA) or ionomeric resin. The polymeric insert may be in the form of amultilayer film with particular functionalities, for instance betteracoustic properties, anti-UV properties, etc.

The thickness of the polymeric insert is between 50 μm and 4 mm.Generally, the thickness of the insert is less than 1 mm. In motorvehicle glazings, the thickness of the polymeric insert isconventionally 0.76 mm.

When the glass sheets are very thin and have a thickness of less than 1mm, it may be advantageous to use a polymeric sheet with a thickness ofgreater than 1 mm, or even greater than 2 or 3 mm, to give the glazingrigidity, without resulting in an excessive weight increase of thestructure.

Conventionally, the insert comprises at least one layer of polyvinylbutyral (or PVB).

The laminated glazing according to the present invention advantageouslyconstitutes a motor vehicle glazing and especially a windshield. Theconstituent sheets of the laminated glazing are bent together beforebeing assembled with the polymeric insert to form the finished product.

The examples below illustrate the invention without limiting its scope.

The table below describes chemical compositions of five differentglasses.

-   -   composition C1: standard clear glass of silicon-sodium-calcium        type    -   composition C2: glass of borosilicate type    -   composition C3: glass of sodium aluminosilicate type    -   composition C4: glass of chemically reinforced aluminosilicate        type, according to the prior art (as described in patent        application WO 2012/177 426)    -   composition C5: glass of alkali-metal-free borosilicate type

TABLE 1 Composition of the glasses used weight % C1 C2 C3 C4 C5 SiO₂71.1 80.6 60.7 61.9 63.6 Al₂O₃ 0.65 2.3 7.7 16.6 16 B₂O₃ 13 13.5 10.7Na₂O 13.8 3.4 13.1 2.9 K₂O 0.25 0.6 9.55 Li₂O CaO 8.75 7.8 MgO 4 8.4 3.40.1 ZnO 0.7

The temperatures Tp of the glasses of compositions C1 to C5 are given inTable 2.

TABLE 2 temperature Tp for each composition described in Table 1 T_(p) =(T_(annealing) + T_(softening))/2 (° C.) C1 (545 + 725)/2 = 635 C2(560 + 821)/2 = 690 C3 (540 + 740)/2 = 640 C4 (609 + 843)/2 = 726 C5(722 + 971)/2 = 846

A laminated glazing in accordance with the present invention ismanufactured using an outer glass sheet of composition C3 1.6 mm thick,a PVB insert 0.76 mm thick and an inner glass sheet of composition C10.55 mm thick. The difference in temperature Tp of these two glasssheets is 5° C.: these two sheets are simultaneously bent.

The glass sheet of composition C3 is particularly capable of beingchemically reinforced by tempering. The assembly of a chemicallyreinforced glass sheet of chemical composition C3 with a thin innerglass sheet of silicon-sodium-calcium glass makes it possible to obtaina laminated glazing of low thickness, with good mechanical strength andfor which the two glass sheets may be simultaneously bent.

For comparative purposes, a laminated glazing is prepared by assemblingan outer glass sheet of composition C4 1 mm thick with a 0.76 mm PVBinsert and an inner glass sheet of composition C1. From a mechanicalviewpoint, the strength tests are acceptable, the outer glass beingchemically reinforced. On the other hand, the difference in temperatureTp between these two glass sheets is 91° C.: the two glass sheets cannotbe bent simultaneously.

In order to compare the resistance of different laminated glazings toprojections of gravel, an indentation test (called «Sarbacane» test) isperformed. This test consists in releasing a weighted (3.2 g weight)Vickers diamond indenter on the outer face of a plate of laminatedglazing 200×200 mm in size, held in a flexible rubber frame, fromdifferent heights (from 100 to 2000 mm). The flexible frame allows thelaminated glazing to be deformed during the impact of the indenter. Thedrop height until a star-shaped crack is visible on inspection with amicroscope, or whose maximum size exceeds 10 mm, after impact on theouter glass sheet (impact depth of between 100 and 150 μm) is thusmeasured. The height is increased by 100 mm between each drop of theindenter and the first height at which the crack is observed is noted.Each laminated glazing is tested at nine different points of impact. Thedrop height value given in the examples below corresponds to the mean ofthe nine fracture height values. The detection of the crack takes placeimmediately after dropping the Vickers indenter.

A laminated glazing is assembled comprising an outer glass sheet ofcomposition C2 1.1 mm thick, a 0.76 mm PVB insert and an inner glasssheet of composition C1 0.55 mm thick. The indentation test (“Sarbacane”test) is performed on this laminated glazing: the mean drop heightmeasured is 1918 mm. For comparative purposes, the same test performedon a laminated glazing consisting of two glass sheets of composition C1with respective thicknesses of 1.1 mm for the outer sheet and 0.55 mmfor the inner sheet leads to a measured mean drop height of 989 mm. Themechanical strength of the laminated glazing according to the presentinvention is satisfactory for the intended applications. Moreover, thedifference in temperature Tp of the two glass sheets is 55° C.: the twoglass sheets are bent simultaneously.

A laminated glazing is assembled comprising an outer glass sheet ofcomposition C5 0.7 mm thick, a 0.76 mm PVB insert and an inner glasssheet of composition C1 0.7 mm thick. The indentation test (“Sarbacane”test) is performed on this laminated glazing: the mean drop heightmeasured is 1960 mm. For comparative purposes, the same test performedon a laminated glazing consisting of two glass sheets of composition C1with respective thicknesses of 0.7 mm for the outer sheet and 0.7 mm forthe inner sheet leads to a measured mean drop height of 633 mm. Themechanical strength of the laminated glazing is satisfactory for theintended applications. However, the difference in temperature Tp of thetwo glass sheets is 211° C.: the two glass sheets cannot be bentsimultaneously. The mechanical strength of this assembly satisfies thedesired criteria, but, on account of the different chemical compositionsof the two glass sheets and of a viscous behavior that is also verydifferent, it is not possible to bend these two sheets together.

The invention claimed is:
 1. A laminated glazing comprising at least oneouter glass sheet, an inner glass sheet and a polymeric insert locatedbetween the outer and inner glass sheets, in which the inner glass sheethas a thickness of not more than 1.5 mm, the outer glass sheet is anon-chemically reinforced glass sheet of different chemical compositionfrom that of the inner glass sheet, a difference between thetemperatures Tp1 and Tp2 being less than 80° C., with temperature Tp1being greater than temperature Tp2, wherein the temperature Tp1 is theaverage of the upper annealing temperature and the softening point ofthe outer glass sheet, and wherein the temperature Tp2 is the average ofthe upper annealing temperature and the softening point of the innerglass sheet, a general formula defining the temperature Tp beingTp=(T _(softening) +T _(annealing))/2 wherein the upper annealingtemperature corresponding to the temperature at which a viscosity of aglass material is 10¹³ poises and the softening point corresponding tothe temperature at which a viscosity of a glass material is 10^(7.6)poises, wherein the laminated glazing is a bent glazing and constitutesa motor vehicle windshield, wherein a thickness of the outer glass sheetis greater than the thickness of the inner glass sheet, and wherein thepolymeric insert has a thickness from 500 μm to 4 mm.
 2. The glazing asclaimed in claim 1, wherein the difference between the temperatures Tp1and Tp2 is less than 70° C.
 3. The glazing as claimed in claim 1,wherein the outer glass sheet has a thickness of not more than 2.1 mm.4. The glazing as claimed in claim 1, wherein the polymeric insertcomprises one or more layers of thermoplastic chosen from polyurethane,polycarbonate, polyvinyl butyral (PVB), polymethyl methacrylate (PMMA)and ethylene-vinyl acetate (EVA) or an ionomeric resin.
 5. The glazingas claimed in claim 4, wherein the polymeric insert comprises at leastone layer made of polyvinyl butyral.
 6. The glazing as claimed in claim1, wherein the outer glass sheet has a chemical composition of aborosilicate glass.
 7. The glazing as claimed in claim 6, wherein theouter glass sheet comprises SiO₂ 75-85%, Al₂O₃  2-3%, B₂O₃ 10-15%,Na₂O + K₂O  3-7%.


8. The glazing as claimed in claim 1, wherein the outer glass sheet hasa chemical composition of a sodium aluminosilicate glass.
 9. The glazingas claimed in claim 8, wherein the outer glass sheet comprises SiO₂55-71%, Al₂O₃  2-15% Na₂O  9-18% MgO  2-11% K₂O  1-15% B₂O₃  0-5%, CaO 0-5% SnO₂  0-5%.


10. The glazing as claimed in claim 9, wherein the outer glass sheetcomprises 4-15% of Al₂O₃.
 11. The glazing as claimed in claim 1, whereinthe inner glass sheet has a thickness of not more than 1.1 mm.
 12. Theglazing as claimed in claim 1, wherein the inner glass sheet has acomposition of a silicon-sodium-calcium glass.
 13. The glazing asclaimed in claim 2, wherein the difference between the temperatures Tp1and Tp2 is less than 60° C.
 14. The glazing as claimed in claim 3,wherein the outer glass sheet has a thickness of not more than 1.6 mm.15. The glazing as claimed in claim 11, wherein the inner glass sheethas a thickness of less than 1 mm.
 16. The glazing as claimed in claim1, wherein the polymeric insert has a thickness from 760 μm to 4 mm.